ANYCUBIC IPHPLGE-107 PLA Filament, 1 kg (gray)
ANYCUBIC IPHPLGE-107 PLA Filament 1 kg (Gray)
ANYCUBIC PLA 1 kg is a high-quality 3D printing filament that delivers consistent and repeatable results thanks to its precise diameter, accurate to within 0.02 mm. The carefully wound spool minimizes the risk of tangling, ensuring a smooth, uninterrupted print. The material is compatible with FDM printers and supports smart identification in the Anycubic ACE Pro system, enabling automatic parameter recognition.
Eco-friendly material and wide range of applications
PLA filament is made from lactic acid obtained through starch fermentation, making it a biodegradable and more environmentally friendly material. The reusable spool with a threaded connection ensures stability and resistance to temperatures up to 80°C. As a result, the filament is suitable for both everyday prints and more demanding projects.
Print precision and extensive color options
The filament is also available in a PLA CMYK (Cyan, Magenta, Yellow, White) variant, which allows for over a million color combinations when used with the Kobra 3 Combo printer. The material’s uniform structure and stable operating parameters make it easy to achieve precise details and an aesthetically pleasing finish on models.
Print parameters and material properties
The recommended nozzle temperature ranges from 190 to 230°C, and the build plate temperature from 55 to 65°C, allowing you to adjust settings for a specific project. The recommended print speed ranges from 50 to 200 mm/s, and the maximum flow rate is 12 mm³/s. The material has a density of 1.24 g/cm³ and a Vicat softening temperature of 55°C, which affects its performance characteristics and ease of processing.
| Manufacturer | Anycubic |
|---|---|
| Model | IPHPLGE-107 |
| Material | PLA |
| Weight | 1 kg |
| Color | gray |
| Compatibility | FDM printers |
| Filament diameter | ±0.02 mm |
| Nozzle temperature | 190–230°C |
| Bed temperature | 55–65°C |
| Recommended print speed | 50–200 mm/s |
| Maximum flow rate | 12 mm³/s |
| Cooling time | 8 s |
| Density | 1.24 g/cm³ |
| Vicat softening temperature | 55°C |
| Deformation resistance (0.45 MPa) | 54°C |
| Material stiffness (Young’s modulus) | 2534 ± 85 MPa |
| Tensile strength | 48 ± 5 MPa |
| Elongation at break | 8 ± 1% |
| Flexural stiffness | 3360 ± 100 MPa |
| Flexural strength | 90 ± 3 MPa |
| Impact resistance (Izod) | 22 ± 1 kJ/m² |
| Tensile strength (Z) | 26 ± 1 MPa |