ELEGOO ASA Filament (Black)
ELEGOO ASA Filament (black)
ELEGOO ASA (acrylonitrile-styrene-acrylic - weather resistant plastic) filament in black will work great for projects that will be exposed to sun, rain or high temperatures. The material will not discolor, will not crack and will remain durable even after a long time outdoors. This makes it well suited for printing garden, technical and decorative elements.
Stability at high temperatures
ASA has higher heat resistance than popular plastics such as PLA (polylactide - a biodegradable plant-based plastic) or PETG (modified polyethylene terephthalate - an easy-to-print, durable material). It does not lose its shape even at temperatures close to 100°C, and its mechanical properties remain stable. In terms of impact resistance, durability and stiffness, it matches ABS (acrylonitrile-butadiene-styrene - a plastic used, among other things, in electronics housings) filament, so it works well in functional projects.
Always clean printing
The filament is precisely wound with a diameter tolerance of ± 0.02 mm, which reduces the risk of jams and ensures even feeding of the material. The cardboard spool is recycled and vacuum-packed with a moisture absorber, so the material doesn't absorb water or form bubbles. Fits most FDM 3D printers (Fused Deposition Modeling - a technology in which material is melted and applied in layers).
General
| Manufacturer | ELEGOO |
|---|---|
| Model | 50.203.0182 |
| Color | Black |
| Weight | 1 kg |
Recommended print settings
| Drying settings before printing | 80 ± 5°C |
|---|---|
| Ambient temperature and humidity | ≤ 80°C, ≤ 20% relative humidity (store with moisture absorber) |
| Nozzle temperature | 240-270 °C |
| Table temperature (depending on printer and surface) | 90 - 100°C |
| Type of working surface | Textured PEI (polyetherimide - a durable, adherent material used as a base for 3D printing) or other compatible surface |
| Printing speed | Less than 270 mm/s |
Physical properties
| Tensile strength (XY - measured in the horizontal plane of the print, where the material is strongest) | 35 ± 2 MPa |
|---|---|
| Elongation at break (XY) | 9,4% ± 2,3% |
| Bending strength (XY) | 65 ± 4 MPa |
| Bending modulus (XY) | 1905 ± 131 MPa |
| Impact strength (XY) | 40.1 ± 3.7 kJ/m² |